KÖSTER FLOOR W-EP UNIVERSAL ANTISLIP

3.5 mm, self-levelling, low-emission (AgBB compliant), water-based epoxy flooring system with broadcast antislip surface and single-color matt finish

Fields of application

Industrial flooring system for indoor applications and horizontal surfaces, suitable for medium-duty in moderate traffic areas, with moderate chemical resistance and functional aesthetics

Sectors

General industry, manufacturing and production halls, workshops, logistics centers, warehouses, domestic/private garages, basements, below-grade areas, technical rooms, retailers, functional floors in residential and commercial buildings, and stairs and corridors

System Build-Up

	Description	Material	Consumption
	Substrate	Concrete / cementitious screed
1	Primer	KÖSTER CT 215 Universal Floor diluted 10 to 25 % with water. The amount of water depends on the substrate porosity.	0.25 kg/m² per layer (approx. 0.20 resin + 0.05 water)
2	Basecoat	KÖSTER CT 215 Universal Floor filled at a ratio 1 : 1 with Filler Fine (CT 710) or similar + 5 % Water (1 l pro 20 kg mix)	3.20 kg/m² (approx. 1.6 resin + 1.6 filler)
3	Broadcast to excess	Quartz Sand 0.4–0.8 mm (CT 488) or similar	4.00 kg/m² (broadcast to excess, approx. 5 kg/m² applied)
4	Topcoat	KÖSTER CT 215 Universal Floor. Matt finish and good cleanability	1.00 kg/m²

Comments

Consumption values are indicative and may vary depending on substrate roughness, temperature and porosity, as well as application-related losses. A typical variation of 20% should be considered.
Depending on substrate conditions (e.g. porosity, roughness), a second primer coat and/or a scratch coat may be required.
Depending on the selected topcoat color (e.g. light or bright colors) and the contrast with the underlying layers, an additional topcoat may be required.
The use of anti-slip particles may reduce gloss and modify the surface texture and appearance.

Application parameters

	Material	Substrate conditions	Application conditions	Mixing regime	Application tools	Pot life / Recoating interval / Ready for traffic
	Concrete / cementitious screed
1	KÖSTER CT 215 Universal Floor diluted 10 to 25 % with water. The amount of water depends on the substrate porosity.	ICRI CSP 3–5 (depending on the expected traffic) by shot blasting Clean, sound and visible dry Tensile strength > 1.5 N/mm² Substrate relative humidity: < 4 % CM Device	Material temperature 15–25 °C Substrate and ambient temperature 10–30 °C Substrate and material temperatures must be ≥ 3 °C above dew point during application and for 24 h.	Electric single or double paddle mixer (300–400 rpm) Mix for 2 min Transfer to a clean container Add water Mix for an additional 1 min and scrape the sides	Rubber Squeegee 40 cm (CT 922 002) Resin Roller 25 cm (CT 961 002) Resin Roller 10 cm (CT 913 001)	Pot life: 60 min. Recoating interval: 10 °C: 24 - 72 h 20 °C: 12 - 48 h 30 °C: 8 - 48 h
2	KÖSTER CT 215 Universal Floor filled at a ratio 1 : 1 with Filler Fine (CT 710) or similar + 5 % Water (1 l pro 20 kg mix)	Previously primed, scratchcoated, sandbroadcast or coated surface. Clean, sound and visible dry Tensile strength > 1.5 N/mm² Substrate relative humidity: < 4 % CM Device	Material temperature 15–25 °C Substrate and ambient temperature 10–30 °C Substrate and material temperatures must be ≥ 3 °C above dew point during application and for 24 h.	Electric single or double paddle mixer (300–400 rpm) Mix for 2 min Transfer to a clean container Add filler Mix for an additional 1 min and scrape the sides Add water Mix for an additional 1 min and scrape the sides	Notched Trowel S3 (CT 933 001) (optionally) Loop Roller 25 cm (CT 911 001) Metallic Spike Roller 25 cm (CT 914 002)	Pot life: 60 min. Recoating interval: 10 °C: 24 - 72 h 20 °C: 12 - 48 h 30 °C: 8 - 48 h
3	Quartz Sand 0.4–0.8 mm (CT 488) or similar
4	KÖSTER CT 215 Universal Floor. Matt finish and good cleanability	Previously primed, scratchcoated, sandbroadcast or coated surface. Clean, sound and visible dry. Tensile strength > 1.5 N/mm² Substrate relative humidity: < 4 % CM Device	Material temperature 15–25 °C Substrate and ambient temperature 10–30 °C Substrate and material temperatures must be ≥ 3 °C above dew point during application and for 24 h.	Electric single or double paddle mixer (300–400 rpm) Mix for 2 min Transfer to a clean container Mix for an additional 1 min and scrape the sides	Rubber Squeegee 40 cm (CT 922 002) Resin Roller 25 cm (CT 961 002) Resin Roller 10 cm (CT 913 001)	Pot life: 60 min. Recoating interval: 10 °C: 24 - 72 h 20 °C: 12 - 48 h 30 °C: 8 - 48 h Ready for light traffic (hours) / fully cured (days): 10 °C: 72 h / 7 d 20 °C: 48 h / 5 d 30 °C: 24 h / 3 d